Public test session report

Winkle Standard Glaciar White PLA High Speed White

MaterialID MAT0164

3DPIceland Labs
Generated with 3DPIceland Engineering Platform v70.0.4 DIRECT-IMPACT-METHODOLOGY - Izod and Charpy Methodology
2026-10-13 19:31:28

Traceability boundary: canonical per-module measured dates are shown below. Session identifier, time of day, operator, printer/slicer profile and environmental conditions are Not recorded and are never inferred.

Measurement provenance

Canonical SQLite measured dates use ISO format; missing dates remain Not recorded.

Module	Measured date
Tensile	Not recorded
Impact	Not recorded
Izod	2026-10-08
Charpy	2026-10-08
Stiffness	Not recorded

Rigid test status
Complete

Rigid result modules
6/6

Rigid specimen/result records
39

Public details
Approved

Rigid specimen and result quality

Module	Orientation	Average	Std. dev.	CV	Specimens	Confidence	Validation
Tensile	Upright	15,073 MPa	4,927 MPa	0,327%	8	8/10	OK
Tensile	Flat	42,051 MPa	7,761 MPa	0,185%	10	10/10	OK
Impact	Upright	8,182 kJ/m²	0,658 kJ/m²	0,08%	10	10/10	OK
Impact	Flat	10,538 kJ/m²	0,911 kJ/m²	0,086%	10	10/10	OK
Stiffness	Three-point bend	3237,057 MPa	n/a	n/a	1	Complete	OK

Recorded native inputs

Module	Input set	Recorded values
Tensile	Upright force inputs (N)	90, 137, 45, 126, 95, 110, 61, 120, ,
Tensile	Flat force inputs (N)	244, 264, 257, 313, 296, 303, 321, 312, 273, 151
Impact	Upright needle inputs (%)	10,00, 10,00, 10,00, 10,00, 11,50, 8,50, 10,00, 9,50, 10,00, 11,00
Impact	Flat needle inputs (%)	12,00, 12,00, 12,00, 14,00, 14,00, 13,00, 14,00, 13,00, 14,00, 11,00
Stiffness	Revolutions / degrees	1 / 210

Approved test notes

Method and equipment context

Purpose-built tensile, pendulum impact and three-point bend apparatus are used with the governed Settings Manager constants consumed by ResultsService. Results are comparative and do not claim accredited-laboratory equipment.

Testing methodology · Engineering methodology whitepaper · Download PDF

Izod and Charpy Impact Strength

Charpy Impact Strength · 2026-10-08
Instrument readings in kJ/m²
Mean 2.368 kJ/m²; Std. Dev 0.327 kJ/m²; CV 13.829%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Izod Impact Strength · 2026-10-08
Instrument readings in kJ/m²
Mean 3.796 kJ/m²; Std. Dev 0.237 kJ/m²; CV 6.251%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.