Public test session report

Winkle Standard Canary Yellow PLA High Speed Yellow

MaterialID MAT0160

3DPIceland Labs
Generated with 3DPIceland Engineering Platform v70.0.4 DIRECT-IMPACT-METHODOLOGY - Izod and Charpy Methodology
2026-10-13 19:31:28

Traceability boundary: canonical per-module measured dates are shown below. Session identifier, time of day, operator, printer/slicer profile and environmental conditions are Not recorded and are never inferred.

Measurement provenance

Canonical SQLite measured dates use ISO format; missing dates remain Not recorded.

Module	Measured date
Tensile	Not recorded
Impact	Not recorded
Izod	2026-10-08
Charpy	2026-10-08
Stiffness	Not recorded

Rigid test status
Complete

Rigid result modules
6/6

Rigid specimen/result records
41

Public details
Approved

Rigid specimen and result quality

Module	Orientation	Average	Std. dev.	CV	Specimens	Confidence	Validation
Tensile	Upright	14,12 MPa	5,669 MPa	0,402%	10	10/10	OK
Tensile	Flat	43,435 MPa	9,609 MPa	0,221%	10	10/10	OK
Impact	Upright	7,153 kJ/m²	1,082 kJ/m²	0,151%	10	10/10	OK
Impact	Flat	8,76 kJ/m²	0,709 kJ/m²	0,081%	10	10/10	OK
Stiffness	Three-point bend	3075,204 MPa	n/a	n/a	1	Complete	OK

Recorded native inputs

Module	Input set	Recorded values
Tensile	Upright force inputs (N)	81, 105, 35, 97, 156, 74, 57, 135, 113, 65
Tensile	Flat force inputs (N)	310, 283, 308, 342, 156, 187, 323, 310, 272, 333
Impact	Upright needle inputs (%)	10,00, 8,00, 10,00, 8,50, 7,50, 9,50, 9,50, 6,00, 9,00, 10,00
Impact	Flat needle inputs (%)	10,00, 10,00, 10,00, 12,00, 12,00, 11,00, 11,00, 11,00, 11,00, 9,50
Stiffness	Revolutions / degrees	1 / 240

Approved test notes

Method and equipment context

Purpose-built tensile, pendulum impact and three-point bend apparatus are used with the governed Settings Manager constants consumed by ResultsService. Results are comparative and do not claim accredited-laboratory equipment.

Testing methodology · Engineering methodology whitepaper · Download PDF

Izod and Charpy Impact Strength

Charpy Impact Strength · 2026-10-08
Instrument readings in kJ/m²
Mean 2.314 kJ/m²; Std. Dev 0.501 kJ/m²; CV 21.632%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Izod Impact Strength · 2026-10-08
Instrument readings in kJ/m²
Mean 3.675 kJ/m²; Std. Dev 0.192 kJ/m²; CV 5.236%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.