Public test session report

Thorwell Standard Silk PLA Silk Blue

MaterialID MAT0147

3DPIceland Labs
Generated with 3DPIceland Engineering Platform v70.0.4 DIRECT-IMPACT-METHODOLOGY - Izod and Charpy Methodology
2026-10-13 19:31:28

Traceability boundary: canonical per-module measured dates are shown below. Session identifier, time of day, operator, printer/slicer profile and environmental conditions are Not recorded and are never inferred.

Measurement provenance

Canonical SQLite measured dates use ISO format; missing dates remain Not recorded.

Module	Measured date
Tensile	Not recorded
Impact	Not recorded
Izod	2026-10-10
Charpy	2026-10-10
Stiffness	Not recorded

Rigid test status
Complete

Rigid result modules
6/6

Rigid specimen/result records
37

Public details
Approved

Rigid specimen and result quality

Module	Orientation	Average	Std. dev.	CV	Specimens	Confidence	Validation
Tensile	Upright	3,23 MPa	1,088 MPa	0,337%	6	6/10	OK
Tensile	Flat	15,319 MPa	3,633 MPa	0,237%	10	10/10	OK
Impact	Upright	3,311 kJ/m²	1,791 kJ/m²	0,541%	10	10/10	OK
Impact	Flat	10,25 kJ/m²	2,046 kJ/m²	0,2%	10	10/10	OK
Stiffness	Three-point bend	1299,382 MPa	n/a	n/a	1	Complete	OK

Recorded native inputs

Module	Input set	Recorded values
Tensile	Upright force inputs (N)	23, 20, 9, 21, 22, 31, , , ,
Tensile	Flat force inputs (N)	74, 118, 115, 48, 115, 112, 86, 116, 96, 116
Impact	Upright needle inputs (%)	1,00, 4,00, 4,50, 7,00, 1,00, 1,50, 5,00, 6,50, 5,50, 5,00
Impact	Flat needle inputs (%)	13,00, 13,00, 15,00, 13,50, 14,00, 14,00, 14,00, 8,00, 13,00, 8,00
Stiffness	Revolutions / degrees	3 / 340

Approved test notes

Method and equipment context

Purpose-built tensile, pendulum impact and three-point bend apparatus are used with the governed Settings Manager constants consumed by ResultsService. Results are comparative and do not claim accredited-laboratory equipment.

Testing methodology · Engineering methodology whitepaper · Download PDF

Izod and Charpy Impact Strength

Charpy Impact Strength · 2026-10-10
Instrument readings in kJ/m²
Mean 13.256 kJ/m²; Std. Dev 2.094 kJ/m²; CV 15.799%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Izod Impact Strength · 2026-10-10
Instrument readings in kJ/m²
Mean 9.968 kJ/m²; Std. Dev 1.503 kJ/m²; CV 15.076%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.