Public printing recommendation

Yasin Standard Gray PLA Gray

MaterialID MAT0127

3DPIceland Labs
Generated with 3DPIceland Engineering Platform v70.0.4 DIRECT-IMPACT-METHODOLOGY - Izod and Charpy Methodology
2026-10-13 19:33:00

Guidance boundary: values below are shared base-material guidance resolved only through the canonical BaseMaterialId link. They are not manufacturer-, spool- or printer-specific validated settings. Missing fields remain Not recorded.

Overall
48/100

Engineering axes
7/8

Public rank
39 / 166

MSRP USD/kg
26.56

Engineering profile

Overall

48/100

Tensile

38/100

Impact

—

Izod

100/100

Charpy

2/100

Stiffness

100/100

Consistency

7/100

Layer adhesion

45/100

Recommended applications

Rigid brackets, fixtures and shape-stable prototypes
Cosmetic parts, concept models or low-load prototypes

Measured strengths

Layer adhesion: 45/100. Z-axis bonding is better than the material-family context.
Izod/Charpy impact family: 51/100. The two-method impact score is competitive against the material-family context.
Tensile: 38/100. Tensile behavior is competitive against the material-family context.
Stiffness: 100/100. Stiffness is a relative advantage in this comparison group.

Limitations

Tensile: 38/100. Avoid using this as the primary choice for tensile-loaded parts.
Consistency: 7/100. Repeatability may not be the best reason to choose this filament.

Engineering trade-offs

The report should be read as a suitability warning rather than a general-purpose recommendation.

Base-material printing guidance

Guidance	Minimum	Recommended	Maximum	Unit
Nozzle temperature	195	230	230	°C
Bed temperature	60	60	70	°C
Print speed	55	165	165	mm/s
Cooling	20	80	85	%

Guidance	Value	Unit
Cooling guidance	High
Drying temperature	50	°C
Drying time	5	hours
Enclosure	Not required
Printer / G-code reference	PrusaCoreOneL
Slicer profile reference	Prusament PLA

Print workflow checks

Confirm nozzle temperature, bed temperature, speed, cooling and drying requirements from the manufacturer profile or spool label.
Print a small validation part before committing to a long, costly or safety-relevant print.
Orient the part so the governing load does not rely on an unverified or weak engineering axis.
Repeatability is low on the internal scale; run extra validation specimens before relying on the profile.

Decision guidance

Use this material mainly for low-load, visual or experimental parts.
Review the listed alternatives if the application needs stronger overall performance.

Stronger same-family alternatives

MaterialID	Material	Manufacturer	Overall	Tensile	Impact	Izod	Charpy
MAT0265	Coex 3D Standard Scarlet Red PLA Red	Coex 3D	58/100	39/100	—	n/a	n/a
MAT0066	ProtoPasta HTPLA Cloverleaf Metallic Green PLA Metal Green	ProtoPasta	56/100	29/100	—	n/a	n/a
MAT0118	Prusa3D Prusament Azure Blue PLA Blue	Prusa3D	55/100	36/100	—	n/a	n/a

Confirm exact settings against the manufacturer profile, spool label and actual printer/material combination. Results do not replace application-specific validation.

Testing methodology · Download PDF

Izod and Charpy Impact Strength

Charpy Impact Strength · 2026-10-05
Instrument readings in kJ/m²
Mean 1.663 kJ/m²; Std. Dev 0.317 kJ/m²; CV 19.083%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Izod Impact Strength · 2026-10-05
Instrument readings in kJ/m²
Mean 2344.974 kJ/m²; Std. Dev 7406.415 kJ/m²; CV 315.842%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Score policy engineering-score-v70-1: Overall requires tensile, stiffness, consistency, layer adhesion and the Izod/Charpy impact family, each with equal weight. Both impact methods and configured versioned references are required. Missing results and unconfigured scores remain n/a. Legacy Impact is historical only; thermal remains separate. Engineering-axis counts describe displayed evidence, not Overall completeness.