Public manufacturer report

Yasin

Portfolio coverage, product-level engineering context and comparative public manufacturer positioning.

3DPIceland Labs
Generated with 3DPIceland Engineering Platform v70.0.4 DIRECT-IMPACT-METHODOLOGY - Izod and Charpy Methodology
2026-10-13 19:31:19

Public-data contract: portfolio statistics and positions use only explicitly allowlisted MaterialIDs and existing Verified Material Summary scores. No measurement or score is recalculated.

Public materials

Product lines

Material types

With results

Complete profiles

Average overall

41/100

Public global rank

20 of 22

Benchmark manufacturers

Manufacturer overview and public global position

Materials	Product lines	Types	With results	Complete	Average overall	Global rank	Portfolio leader	Strongest axis	With MSRP	With video
27	1	14	24	23	41/100	20 of 22	Yasin Standard Black PA6 CF Black	stiffness	27	5

Manufacturer website: Open manufacturer website

Category position by base material

Base material	Public manufacturer position	Average overall	Scored products
ABS	3 of 5	45/100	1
ASA	3 of 5	40,7/100	3
HIPS	1 of 1	42/100	1
PA12	6 of 6	35/100	2
PA6	4 of 4	46/100	3
PC	4 of 4	31/100	1
PCTG	3 of 4	35/100	1
PEBA	n/a	n/a	0
PETG	2 of 12	45,3/100	3
PLA	16 of 17	41,6/100	5
PMMA	1 of 1	36/100	1
POM	1 of 1	42/100	1
PVA	1 of 1	37/100	1
TPE	n/a	n/a	0

Overall leaders

Yasin Standard Black PA6 CF Black

48/100

Yasin Standard Black PA6 GF Black

48/100

Yasin Standard Gray PLA Gray

48/100

Yasin Standard Black PETG CF Black

47/100

Yasin Standard Silk PLA Silk Pink

46/100

Yasin Standard Blue ABS Blue

45/100

Yasin Standard Gray PETG Gray

45/100

Yasin Standard Black PETG GF Black

44/100

Yasin Standard Black ASA GF Black

42/100

Yasin Standard White HIPS White

42/100

Consistency leaders

Yasin Standard Silk PLA Silk Pink

88/100

Yasin Standard Soft PLA PLA Soft White

87/100

Yasin Standard Black ASA CF Black

86/100

Yasin Standard Gray PETG Gray

86/100

Yasin Standard Black PA12 CF Black

85/100

Yasin Standard Black PA6 CF Black

82/100

Yasin Standard Black PETG CF Black

81/100

Yasin Standard Black PA6 GF Black

80/100

Yasin Standard Clear PMMA Clear

79/100

Yasin Standard Black ASA GF Black

77/100

Product-level engineering context

MaterialID	Material	Product line	Type	Reinforcement	Rigid coverage	Engineering axes	Overall	Tensile	Impact	Izod	Charpy	Stiffness	Consistency	Layer adhesion	Strongest axis	MSRP USD/kg	Product	Video
MAT0241	Yasin Standard Blue ABS Blue	Standard	ABS		Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1	7/8	45/100	17/100	—	31/100	68/100	71/100	71/100	15/100	stiffness	$25.44	Product page	n/a
MAT0009	Yasin Standard Black ASA CF Black	Standard	ASA	CF	Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1	7/8	40/100	20/100	—	6/100	7/100	63/100	86/100	25/100	consistency	$33.44	Product page	n/a
MAT0010	Yasin Standard Black ASA GF Black	Standard	ASA	GF	Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1	7/8	42/100	21/100	—	25/100	30/100	65/100	77/100	23/100	consistency	$28.80	Product page	n/a
MAT0017	Yasin Standard White ASA White	Standard	ASA		Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1	7/8	40/100	21/100	—	38/100	42/100	52/100	66/100	22/100	consistency	$27.52	Product page	n/a
MAT0240	Yasin Standard White HIPS White	Standard	HIPS		Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1	7/8	42/100	12/100	—	48/100	49/100	66/100	72/100	11/100	consistency	$26.88	Product page	n/a
MAT0021	Yasin Standard Black PA12 Black	Standard	PA12		Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1	7/8	31/100	22/100	—	4/100	4/100	44/100	74/100	9/100	consistency	$53.12	Product page	n/a
MAT0239	Yasin Standard Black PA12 CF Black	Standard	PA12	CF	Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1	7/8	39/100	33/100	—	5/100	6/100	64/100	85/100	7/100	consistency	$64.48	Product page	n/a
MAT0024	Yasin Standard Black PA6 CF Black	Standard	PA6	CF	Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1	7/8	48/100	41/100	—	7/100	7/100	100/100	82/100	10/100	stiffness	$32.96	Product page	n/a
MAT0026	Yasin Standard Black PA6 GF Black	Standard	PA6	GF	Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1	7/8	48/100	44/100	—	6/100	5/100	99/100	80/100	13/100	stiffness	$30.56	Product page	n/a
MAT0027	Yasin Standard Clear PA6 Clear	Standard	PA6		Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1	7/8	42/100	42/100	—	4/100	3/100	85/100	74/100	8/100	stiffness	$30.24	Product page	n/a
MAT0034	Yasin Standard Black PC Plus Black	Standard	PC		Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1	7/8	31/100	12/100	—	5/100	4/100	59/100	67/100	14/100	consistency	$31.52	Product page	n/a
MAT0238	Yasin Standard Green PCTG Green	Standard	PCTG		Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1	7/8	35/100	22/100	—	3/100	2/100	53/100	67/100	30/100	consistency	$33.44	Product page	n/a
MAT0262	Yasin Standard Blue PEBA Blue	Standard	PEBA		No native results; 0/5 score families; Izod/Charpy 0/2 measured, 0/2 scored; Overall unavailable: missing measurements or references; policy engineering-score-v70-1	0/8	—	—	—	—	—	—	—	—	mechanical profile	$64.16	Product page	n/a
MAT0263	Yasin Standard Clear PEBA Clear	Standard	PEBA		No native results; 0/5 score families; Izod/Charpy 0/2 measured, 0/2 scored; Overall unavailable: missing measurements or references; policy engineering-score-v70-1	0/8	—	—	—	—	—	—	—	—	mechanical profile	$64.16	Product page	n/a
MAT0236	Yasin Standard Black PETG CF Black	Standard	PETG	CF	Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1	7/8	47/100	30/100	—	6/100	5/100	100/100	81/100	18/100	stiffness	$30.56	Product page	n/a
MAT0235	Yasin Standard Black PETG GF Black	Standard	PETG	GF	Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1	7/8	44/100	27/100	—	7/100	8/100	90/100	77/100	16/100	stiffness	$28.16	Product page	n/a
MAT0055	Yasin Standard Gray PETG Gray	Standard	PETG		Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1	7/8	45/100	34/100	—	4/100	3/100	70/100	86/100	31/100	consistency	$24.00	Product page	Video review
MAT0234	Yasin Standard Black PLA CF Black	Standard	PLA	CF	Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1	7/8	41/100	26/100	—	8/100	7/100	86/100	76/100	10/100	stiffness	$32.56	Product page	n/a
MAT0127	Yasin Standard Gray PLA Gray	Standard	PLA		Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1	7/8	48/100	38/100	—	100/100	2/100	100/100	7/100	45/100	Izod impact resistance	$26.56	Product page	Video review
MAT0091	Yasin Standard Silk PLA Silk Pink	Standard	PLA		Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1	7/8	46/100	32/100	—	5/100	4/100	93/100	88/100	11/100	stiffness	$26.56	Product page	Video review
MAT0094	Yasin Standard Soft PLA PLA Soft White	Standard	PLA		Partial; 4/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall unavailable: missing measurements or references; policy engineering-score-v70-1	5/8	—	8/100	—	33/100	49/100	—	87/100	37/100	consistency	$29.44	Product page	Video review
MAT0233	Yasin Standard White PLA matt White	Standard	PLA		Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1	7/8	40/100	15/100	—	15/100	22/100	85/100	69/100	13/100	stiffness	$25.44	Product page	n/a
MAT0145	Yasin Standard Wood PLA Wood Wood Brown	Standard	PLA	Wood	Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1	7/8	33/100	19/100	—	12/100	4/100	77/100	48/100	13/100	stiffness	$29.68	Product page	Video review
MAT0035	Yasin Standard Clear PMMA Clear	Standard	PMMA		Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1	7/8	36/100	20/100	—	4/100	4/100	30/100	79/100	46/100	consistency	$36.80	Product page	n/a
MAT0232	Yasin Standard Natural POM Natural	Standard	POM		Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1	7/8	42/100	29/100	—	10/100	11/100	63/100	76/100	31/100	consistency	$36.64	Product page	n/a
MAT0231	Yasin Standard Clear PVA Clear	Standard	PVA		Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1	7/8	37/100	6/100	—	8/100	11/100	100/100	58/100	11/100	stiffness	$67.20	Product page	n/a
MAT0258	Yasin Standard Black TPE Black	Standard	TPE		No native results; 0/5 score families; Izod/Charpy 0/2 measured, 0/2 scored; Overall unavailable: missing measurements or references; policy engineering-score-v70-1	0/8	—	—	—	—	—	—	—	—	mechanical profile	$52.16	Product page	n/a

Results are comparative 3DPIceland measurements and do not replace manufacturer datasheets or accredited laboratory testing.

Testing methodology · Engineering methodology whitepaper · Download PDF

Yasin Standard Blue ABS Blue

Izod and Charpy Impact Strength

Izod Impact Strength · 2026-10-06
Instrument readings in kJ/m²
Mean 24.455 kJ/m²; Std. Dev 2.8 kJ/m²; CV 11.449%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Charpy Impact Strength · 2026-10-06
Instrument readings in kJ/m²
Mean 54.204 kJ/m²; Std. Dev 5.897 kJ/m²; CV 10.879%; Samples 9; Confidence 9
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Yasin Standard Black ASA CF Black

Izod and Charpy Impact Strength

Izod Impact Strength · 2026-10-02
Instrument readings in kJ/m²
Mean 5.07 kJ/m²; Std. Dev 0.134 kJ/m²; CV 2.636%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Charpy Impact Strength · 2026-10-02
Instrument readings in kJ/m²
Mean 5.3 kJ/m²; Std. Dev 0.101 kJ/m²; CV 1.905%; Samples 9; Confidence 9
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Yasin Standard Black ASA GF Black

Izod and Charpy Impact Strength

Izod Impact Strength · 2026-10-03
Instrument readings in kJ/m²
Mean 19.916 kJ/m²; Std. Dev 1.833 kJ/m²; CV 9.205%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Charpy Impact Strength · 2026-10-03
Instrument readings in kJ/m²
Mean 24.332 kJ/m²; Std. Dev 5.763 kJ/m²; CV 23.683%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Yasin Standard White ASA White

Izod and Charpy Impact Strength

Izod Impact Strength · 2026-10-06
Instrument readings in kJ/m²
Mean 30.509 kJ/m²; Std. Dev 10.463 kJ/m²; CV 34.294%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Charpy Impact Strength · 2026-10-06
Instrument readings in kJ/m²
Mean 33.355 kJ/m²; Std. Dev 17.697 kJ/m²; CV 53.056%; Samples 8; Confidence 8
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Yasin Standard White HIPS White

Izod and Charpy Impact Strength

Izod Impact Strength · 2026-10-06
Instrument readings in kJ/m²
Mean 38.196 kJ/m²; Std. Dev 3.111 kJ/m²; CV 8.145%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Charpy Impact Strength · 2026-10-06
Instrument readings in kJ/m²
Mean 39.401 kJ/m²; Std. Dev 5.476 kJ/m²; CV 13.898%; Samples 7; Confidence 7
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Yasin Standard Black PA12 Black

Izod and Charpy Impact Strength

Izod Impact Strength · 2026-10-07
Instrument readings in kJ/m²
Mean 3.12 kJ/m²; Std. Dev 0.428 kJ/m²; CV 13.727%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Charpy Impact Strength · 2026-10-07
Instrument readings in kJ/m²
Mean 3.1 kJ/m²; Std. Dev 0.777 kJ/m²; CV 25.053%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Yasin Standard Black PA12 CF Black

Izod and Charpy Impact Strength

Izod Impact Strength · 2026-10-04
Instrument readings in kJ/m²
Mean 4.373 kJ/m²; Std. Dev 0.127 kJ/m²; CV 2.91%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Charpy Impact Strength · 2026-10-04
Instrument readings in kJ/m²
Mean 4.7 kJ/m²; Std. Dev 0.44 kJ/m²; CV 9.353%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Yasin Standard Black PA6 CF Black

Izod and Charpy Impact Strength

Izod Impact Strength · 2026-10-01
Instrument readings in kJ/m²
Mean 5.898 kJ/m²; Std. Dev 0.458 kJ/m²; CV 7.76%; Samples 9; Confidence 9
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Charpy Impact Strength · 2026-10-01
Instrument readings in kJ/m²
Mean 5.716 kJ/m²; Std. Dev 0.316 kJ/m²; CV 5.535%; Samples 9; Confidence 9
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Yasin Standard Black PA6 GF Black

Izod and Charpy Impact Strength

Izod Impact Strength · 2026-10-02
Instrument readings in kJ/m²
Mean 4.672 kJ/m²; Std. Dev 0.484 kJ/m²; CV 10.357%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Charpy Impact Strength · 2026-10-02
Instrument readings in kJ/m²
Mean 4.397 kJ/m²; Std. Dev 0.775 kJ/m²; CV 17.629%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Yasin Standard Clear PA6 Clear

Izod and Charpy Impact Strength

Charpy Impact Strength · 2026-10-06
Instrument readings in kJ/m²
Mean 2.772 kJ/m²; Std. Dev 0.053 kJ/m²; CV 1.926%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Izod Impact Strength · 2026-10-06
Instrument readings in kJ/m²
Mean 3.021 kJ/m²; Std. Dev 0.806 kJ/m²; CV 26.667%; Samples 8; Confidence 8
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Yasin Standard Black PC Plus Black

Izod and Charpy Impact Strength

Charpy Impact Strength · 2026-10-03
Instrument readings in kJ/m²
Mean 2.989 kJ/m²; Std. Dev 1.03 kJ/m²; CV 34.45%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Izod Impact Strength · 2026-10-03
Instrument readings in kJ/m²
Mean 4.159 kJ/m²; Std. Dev 0.472 kJ/m²; CV 11.358%; Samples 9; Confidence 9
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Yasin Standard Green PCTG Green

Izod and Charpy Impact Strength

Izod Impact Strength · 2026-10-05
Instrument readings in kJ/m²
Mean 2.253 kJ/m²; Std. Dev 0.675 kJ/m²; CV 29.971%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Charpy Impact Strength · 2026-10-05
Instrument readings in kJ/m²
Mean 1.286 kJ/m²; Std. Dev 0.143 kJ/m²; CV 11.117%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Yasin Standard Blue PEBA Blue

Flexible Material Testing

Comparative in-house measurements; n = independent specimens. Separate test groups; Overall unchanged.

Method	Result	Condition	Mean	n	SD	CV %	Range
eaacea91	Apparent Compressive Stress at 20% Strain (MPa)	10 s hold · 2 mm displacement · cycle 1	4.162	10	0.09	2.164	3.961–4.276
eaacea91	Apparent Compressive Stress at 20% Strain (MPa)	30 s hold · 2 mm displacement · cycle 1	4.041	10	0.093	2.308	3.835–4.15
eaacea91	Compression Force at 20% Strain (N)	10 s hold · 2 mm displacement · cycle 1	264.8	10	5.731	2.164	252–272
eaacea91	Compression Force at 20% Strain (N)	30 s hold · 2 mm displacement · cycle 1	257.1	10	5.934	2.308	244–264
eaacea91	Force reduction from 10 s to 30 s at 20% Strain (%)	first compression only · 2 mm displacement	2.91	10	0.275	9.452	2.222–3.175
eaacea91	Force retention at 20% Strain (%)	10–30 s · 2 mm displacement · cycle 1	97.09	10	0.275	0.283	96.825–97.778
eaacea91	Residual height loss after recovery (%)	20% compression · 30 s compressed hold · 60 s rest · 10 mm initial height · cycle 1	2.29	10	0.12	5.228	2.1–2.5
ed381ba8	Shore A Hardness (Shore A)	10 s reading · 8 mm	92.74	1	—	—	92.74–92.74

Shore location statistics

Within each specimen; specimen numbers are local to each test group. SD uses the sample formula. These readings do not increase independent n.

Method	Scale	Condition	Specimen	Readings	Mean	Location SD	Location CV %
ed381ba8	Shore A Hardness	10 s reading · 8 mm	1	5	92.74	1.436	1.549

Yasin Standard Clear PEBA Clear

Flexible Material Testing

Comparative in-house measurements; n = independent specimens. Separate test groups; Overall unchanged.

Method	Result	Condition	Mean	n	SD	CV %	Range
eaacea91	Apparent Compressive Stress at 20% Strain (MPa)	10 s hold · 2 mm displacement · cycle 1	4.345	10	0.07	1.602	4.244–4.448
eaacea91	Apparent Compressive Stress at 20% Strain (MPa)	30 s hold · 2 mm displacement · cycle 1	4.224	10	0.066	1.57	4.134–4.338
eaacea91	Compression Force at 20% Strain (N)	10 s hold · 2 mm displacement · cycle 1	276.4	10	4.427	1.602	270–283
eaacea91	Compression Force at 20% Strain (N)	30 s hold · 2 mm displacement · cycle 1	268.7	10	4.218	1.57	263–276
eaacea91	Force reduction from 10 s to 30 s at 20% Strain (%)	first compression only · 2 mm displacement	2.785	10	0.327	11.754	2.473–3.546
eaacea91	Force retention at 20% Strain (%)	10–30 s · 2 mm displacement · cycle 1	97.215	10	0.327	0.337	96.454–97.527
eaacea91	Residual height loss after recovery (%)	20% compression · 30 s compressed hold · 60 s rest · 10 mm initial height · cycle 1	2.8	10	0.125	4.454	2.6–3
ed381ba8	Shore A Hardness (Shore A)	10 s reading · 8 mm	92.5	1	—	—	92.5–92.5
eaacea91	Shore A Hardness (Shore A)	10 s reading · 8 mm	91	1	—	—	91–91

Shore location statistics

Within each specimen; specimen numbers are local to each test group. SD uses the sample formula. These readings do not increase independent n.

Method	Scale	Condition	Specimen	Readings	Mean	Location SD	Location CV %
ed381ba8	Shore A Hardness	10 s reading · 8 mm	1	5	92.5	0.5	0.541
eaacea91	Shore A Hardness	10 s reading · 8 mm	1	1	91	—	—

Yasin Standard Black PETG CF Black

Izod and Charpy Impact Strength

Charpy Impact Strength · 2026-09-30
Instrument readings in kJ/m²
Mean 4.298 kJ/m²; Std. Dev 0.426 kJ/m²; CV 9.903%; Samples 9; Confidence 9
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Izod Impact Strength · 2026-09-30
Instrument readings in kJ/m²
Mean 4.467 kJ/m²; Std. Dev 0.239 kJ/m²; CV 5.352%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Yasin Standard Black PETG GF Black

Izod and Charpy Impact Strength

Izod Impact Strength · 2026-09-30
Instrument readings in kJ/m²
Mean 5.867 kJ/m²; Std. Dev 0.103 kJ/m²; CV 1.762%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Charpy Impact Strength · 2026-09-30
Instrument readings in kJ/m²
Mean 6.159 kJ/m²; Std. Dev 0.2 kJ/m²; CV 3.245%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Yasin Standard Gray PETG Gray

Izod and Charpy Impact Strength

Izod Impact Strength · 2026-10-05
Instrument readings in kJ/m²
Mean 3.561 kJ/m²; Std. Dev 0.173 kJ/m²; CV 4.862%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Charpy Impact Strength · 2026-10-05
Instrument readings in kJ/m²
Mean 2.79 kJ/m²; Std. Dev 0.034 kJ/m²; CV 1.202%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Yasin Standard Black PLA CF Black

Izod and Charpy Impact Strength

Charpy Impact Strength · 2026-09-28
Instrument readings in kJ/m²
Mean 5.204 kJ/m²; Std. Dev 0.33 kJ/m²; CV 6.348%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Izod Impact Strength · 2026-09-29
Instrument readings in kJ/m²
Mean 6.324 kJ/m²; Std. Dev 0.61 kJ/m²; CV 9.647%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Yasin Standard Gray PLA Gray

Izod and Charpy Impact Strength

Charpy Impact Strength · 2026-10-05
Instrument readings in kJ/m²
Mean 1.663 kJ/m²; Std. Dev 0.317 kJ/m²; CV 19.083%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Izod Impact Strength · 2026-10-05
Instrument readings in kJ/m²
Mean 2344.974 kJ/m²; Std. Dev 7406.415 kJ/m²; CV 315.842%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Yasin Standard Silk PLA Silk Pink

Izod and Charpy Impact Strength

Charpy Impact Strength · 2026-10-05
Instrument readings in kJ/m²
Mean 2.928 kJ/m²; Std. Dev 0.162 kJ/m²; CV 5.518%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Izod Impact Strength · 2026-10-05
Instrument readings in kJ/m²
Mean 3.911 kJ/m²; Std. Dev 0.231 kJ/m²; CV 5.899%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Yasin Standard Soft PLA PLA Soft White

Flexible Material Testing

Comparative in-house measurements; n = independent specimens. Separate test groups; Overall unchanged.

Method	Result	Condition	Mean	n	SD	CV %	Range
eaacea91	Apparent Compressive Stress at 20% Strain (MPa)	10 s hold · 2 mm displacement · cycle 1	6.262	10	0.106	1.691	6.099–6.413
eaacea91	Apparent Compressive Stress at 20% Strain (MPa)	30 s hold · 2 mm displacement · cycle 1	6.046	10	0.095	1.571	5.879–6.193
eaacea91	Compression Force at 20% Strain (N)	10 s hold · 2 mm displacement · cycle 1	398.4	10	6.736	1.691	388–408
eaacea91	Compression Force at 20% Strain (N)	30 s hold · 2 mm displacement · cycle 1	384.6	10	6.041	1.571	374–394
eaacea91	Force reduction from 10 s to 30 s at 20% Strain (%)	first compression only · 2 mm displacement	3.462	10	0.302	8.737	2.813–3.769
eaacea91	Force retention at 20% Strain (%)	10–30 s · 2 mm displacement · cycle 1	96.538	10	0.302	0.313	96.231–97.187
eaacea91	Residual height loss after recovery (%)	20% compression · 30 s compressed hold · 60 s rest · 10 mm initial height · cycle 1	4.06	10	0.158	3.886	3.7–4.3
ed381ba8	Shore A Hardness (Shore A)	10 s reading · 8 mm	93	1	—	—	93–93

Shore location statistics

Within each specimen; specimen numbers are local to each test group. SD uses the sample formula. These readings do not increase independent n.

Method	Scale	Condition	Specimen	Readings	Mean	Location SD	Location CV %
ed381ba8	Shore A Hardness	10 s reading · 8 mm	1	5	93	2.031	2.184

Izod and Charpy Impact Strength

Charpy Impact Strength · 2026-10-03
Instrument readings in kJ/m²
Mean 39.349 kJ/m²; Std. Dev 3.768 kJ/m²; CV 9.576%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Izod Impact Strength · 2026-10-03
Instrument readings in kJ/m²
Mean 26.715 kJ/m²; Std. Dev 2.097 kJ/m²; CV 7.851%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Yasin Standard White PLA matt White

Izod and Charpy Impact Strength

Izod Impact Strength · 2026-10-03
Instrument readings in kJ/m²
Mean 11.935 kJ/m²; Std. Dev 1.579 kJ/m²; CV 13.23%; Samples 9; Confidence 9
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Charpy Impact Strength · 2026-10-03
Instrument readings in kJ/m²
Mean 17.495 kJ/m²; Std. Dev 2.716 kJ/m²; CV 15.523%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Yasin Standard Wood PLA Wood Wood Brown

Izod and Charpy Impact Strength

Izod Impact Strength · 2026-10-03
Instrument readings in kJ/m²
Mean 9.363 kJ/m²; Std. Dev 13.388 kJ/m²; CV 142.982%; Samples 9; Confidence 9
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Charpy Impact Strength · 2026-10-03
Instrument readings in kJ/m²
Mean 3.444 kJ/m²; Std. Dev 0.094 kJ/m²; CV 2.721%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Yasin Standard Clear PMMA Clear

Izod and Charpy Impact Strength

Charpy Impact Strength · 2026-10-04
Instrument readings in kJ/m²
Mean 3.039 kJ/m²; Std. Dev 0.566 kJ/m²; CV 18.631%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Izod Impact Strength · 2026-10-04
Instrument readings in kJ/m²
Mean 3.005 kJ/m²; Std. Dev 0.152 kJ/m²; CV 5.045%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Yasin Standard Natural POM Natural

Izod and Charpy Impact Strength

Izod Impact Strength · 2026-10-05
Instrument readings in kJ/m²
Mean 8.115 kJ/m²; Std. Dev 1.205 kJ/m²; CV 14.855%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Charpy Impact Strength · 2026-10-05
Instrument readings in kJ/m²
Mean 9.056 kJ/m²; Std. Dev 1.901 kJ/m²; CV 20.988%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Yasin Standard Clear PVA Clear

Izod and Charpy Impact Strength

Izod Impact Strength · 2026-10-03
Instrument readings in kJ/m²
Mean 6.351 kJ/m²; Std. Dev 1.112 kJ/m²; CV 17.513%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Charpy Impact Strength · 2026-10-03
Instrument readings in kJ/m²
Mean 8.593 kJ/m²; Std. Dev 4.095 kJ/m²; CV 47.66%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.

Yasin Standard Black TPE Black

Flexible Material Testing

Comparative in-house measurements; n = independent specimens. Separate test groups; Overall unchanged.

Method	Result	Condition	Mean	n	SD	CV %	Range
eaacea91	Apparent Compressive Stress at 20% Strain (MPa)	10 s hold · 2 mm displacement · cycle 1	1.93	8	0.065	3.366	1.839–2.012
eaacea91	Apparent Compressive Stress at 20% Strain (MPa)	30 s hold · 2 mm displacement · cycle 1	1.802	8	0.068	3.758	1.713–1.902
eaacea91	Compression Force at 20% Strain (N)	10 s hold · 2 mm displacement · cycle 1	122.75	8	4.132	3.366	117–128
eaacea91	Compression Force at 20% Strain (N)	30 s hold · 2 mm displacement · cycle 1	114.625	8	4.307	3.758	109–121
eaacea91	Force reduction from 10 s to 30 s at 20% Strain (%)	first compression only · 2 mm displacement	6.624	8	1.158	17.487	4.724–8.594
eaacea91	Force retention at 20% Strain (%)	10–30 s · 2 mm displacement · cycle 1	93.376	8	1.158	1.241	91.406–95.276
eaacea91	Residual height loss after recovery (%)	20% compression · 30 s compressed hold · 60 s rest · 10 mm initial height · cycle 1	3.463	8	0.501	14.476	3–4.6
ed381ba8	Shore A Hardness (Shore A)	10 s reading · 8 mm	79.3	1	—	—	79.3–79.3

Shore location statistics

Within each specimen; specimen numbers are local to each test group. SD uses the sample formula. These readings do not increase independent n.

Method	Scale	Condition	Specimen	Readings	Mean	Location SD	Location CV %
ed381ba8	Shore A Hardness	10 s reading · 8 mm	1	5	79.3	1.304	1.644

Score policy engineering-score-v70-1: Overall requires tensile, stiffness, consistency, layer adhesion and the Izod/Charpy impact family, each with equal weight. Both impact methods and configured versioned references are required. Missing results and unconfigured scores remain n/a. Legacy Impact is historical only; thermal remains separate. Engineering-axis counts describe displayed evidence, not Overall completeness.