Thorwell
Portfolio coverage, product-level engineering context and comparative public manufacturer positioning.
3DPIceland Labs
Generated with 3DPIceland Engineering Platform v70.0.4 DIRECT-IMPACT-METHODOLOGY - Izod and Charpy Methodology
2026-10-13 19:31:19
Manufacturer overview and public global position
| Materials | Product lines | Types | With results | Complete | Average overall | Global rank | Portfolio leader | Strongest axis | With MSRP | With video |
|---|---|---|---|---|---|---|---|---|---|---|
| 14 | 1 | 7 | 12 | 8 | 42,4/100 | 16 of 22 | Thorwell Standard PLA Plus PLA Plus White | stiffness | 14 | 4 |
Category position by base material
| Base material | Public manufacturer position | Average overall | Scored products |
|---|---|---|---|
| ABS | n/a | n/a | 0 |
| ASA | n/a | n/a | 0 |
| HIPS | n/a | n/a | 0 |
| PETG | 11 of 12 | 35,5/100 | 2 |
| PLA | 12 of 17 | 44,7/100 | 6 |
| TPE | n/a | n/a | 0 |
| TPU | n/a | n/a | 0 |
Overall leaders
Consistency leaders
Product-level engineering context
| MaterialID | Material | Product line | Type | Reinforcement | Rigid coverage | Engineering axes | Overall | Tensile | Impact | Izod | Charpy | Stiffness | Consistency | Layer adhesion | Strongest axis | MSRP USD/kg | Product | Video |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| MAT0152 | Thorwell Standard ABS ABS Yellow | Standard | ABS | Partial; 4/5 score families; Izod/Charpy 0/2 measured, 0/2 scored; Overall unavailable: missing measurements or references; policy engineering-score-v70-1 | 5/8 | — | 20/100 | — | — | — | 72/100 | 58/100 | 12/100 | stiffness | $36.00 | Product page | n/a | |
| MAT0148 | Thorwell Standard ASA ASA Yellow | Standard | ASA | Partial; 4/5 score families; Izod/Charpy 0/2 measured, 0/2 scored; Overall unavailable: missing measurements or references; policy engineering-score-v70-1 | 5/8 | — | 22/100 | — | — | — | 68/100 | 64/100 | 10/100 | stiffness | $33.60 | Product page | n/a | |
| MAT0146 | Thorwell Standard HIPS HIPS Blue | Standard | HIPS | Partial; 4/5 score families; Izod/Charpy 0/2 measured, 0/2 scored; Overall unavailable: missing measurements or references; policy engineering-score-v70-1 | 5/8 | — | 14/100 | — | — | — | 63/100 | 67/100 | 11/100 | consistency | $32.00 | Product page | n/a | |
| MAT0151 | Thorwell Standard Carbon Fiber-T PETG CF Black | Standard | PETG | CF | Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1 | 7/8 | 33/100 | 15/100 | — | 3/100 | 2/100 | 70/100 | 64/100 | 13/100 | stiffness | $40.00 | Product page | n/a |
| MAT0150 | Thorwell Standard PETG PETG Red | Standard | PETG | Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1 | 7/8 | 38/100 | 28/100 | — | 5/100 | 3/100 | 51/100 | 86/100 | 22/100 | consistency | $38.40 | Product page | n/a | |
| MAT0156 | Thorwell Standard PLA Black | Standard | PLA | Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1 | 7/8 | 47/100 | 31/100 | — | 5/100 | 4/100 | 95/100 | 78/100 | 29/100 | stiffness | $30.00 | Product page | Video review | |
| MAT0119 | Thorwell Standard PLA Blue | Standard | PLA | Partial; 4/5 score families; Izod/Charpy 0/2 measured, 0/2 scored; Overall unavailable: missing measurements or references; policy engineering-score-v70-1 | 4/8 | — | 32/100 | — | — | — | 86/100 | 83/100 | 28/100 | stiffness | $30.00 | Product page | Video review | |
| MAT0154 | Thorwell Standard PLA Plus PLA Plus White | Standard | PLA | Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1 | 7/8 | 52/100 | 36/100 | — | 6/100 | 4/100 | 88/100 | 85/100 | 44/100 | stiffness | $32.00 | Product page | n/a | |
| MAT0155 | Thorwell Standard PLA White | Standard | PLA | Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1 | 7/8 | 51/100 | 36/100 | — | 5/100 | 4/100 | 99/100 | 85/100 | 31/100 | stiffness | $30.00 | Product page | Video review | |
| MAT0142 | Thorwell Standard PLA Yellow | Standard | PLA | Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1 | 7/8 | 46/100 | 35/100 | — | 6/100 | 4/100 | 83/100 | 82/100 | 25/100 | stiffness | $30.00 | Product page | Video review | |
| MAT0147 | Thorwell Standard Silk PLA Silk Blue | Standard | PLA | Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1 | 7/8 | 33/100 | 12/100 | — | 12/100 | 17/100 | 43/100 | 76/100 | 21/100 | consistency | $32.00 | Product page | n/a | |
| MAT0153 | Thorwell Standard Wood PLA Wood Brown | Standard | PLA | Wood | Complete; 5/5 score families; Izod/Charpy 2/2 measured, 2/2 scored; Overall eligible; policy engineering-score-v70-1 | 7/8 | 39/100 | 15/100 | — | 4/100 | 4/100 | 83/100 | 83/100 | 12/100 | stiffness | $45.20 | Product page | n/a |
| MAT0259 | Thorwell Standard Blue TPE Blue | Standard | TPE | No native results; 0/5 score families; Izod/Charpy 0/2 measured, 0/2 scored; Overall unavailable: missing measurements or references; policy engineering-score-v70-1 | 0/8 | — | — | — | — | — | — | — | — | mechanical profile | $40.00 | Product page | n/a | |
| MAT0260 | Thorwell Standard Blue TPU Blue | Standard | TPU | No native results; 0/5 score families; Izod/Charpy 0/2 measured, 0/2 scored; Overall unavailable: missing measurements or references; policy engineering-score-v70-1 | 0/8 | — | — | — | — | — | — | — | — | mechanical profile | $40.00 | Product page | n/a |
Testing methodology · Engineering methodology whitepaper · Download PDF
Thorwell Standard Carbon Fiber-T PETG CF Black
Izod and Charpy Impact Strength
Charpy Impact Strength · 2026-10-05
Instrument readings in kJ/m²
Mean 1.668 kJ/m²; Std. Dev 0.552 kJ/m²; CV 33.068%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.
Izod Impact Strength · 2026-10-05
Instrument readings in kJ/m²
Mean 2.023 kJ/m²; Std. Dev 0.604 kJ/m²; CV 29.872%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.
Thorwell Standard PETG PETG Red
Izod and Charpy Impact Strength
Izod Impact Strength · 2026-10-11
Instrument readings in kJ/m²
Mean 3.728 kJ/m²; Std. Dev 0.175 kJ/m²; CV 4.693%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.
Charpy Impact Strength · 2026-10-11
Instrument readings in kJ/m²
Mean 2.756 kJ/m²; Std. Dev 0.048 kJ/m²; CV 1.729%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.
Thorwell Standard PLA Black
Izod and Charpy Impact Strength
Charpy Impact Strength · 2026-10-10
Instrument readings in kJ/m²
Mean 2.944 kJ/m²; Std. Dev 0.106 kJ/m²; CV 3.593%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.
Izod Impact Strength · 2026-10-10
Instrument readings in kJ/m²
Mean 4.108 kJ/m²; Std. Dev 0.404 kJ/m²; CV 9.838%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.
Thorwell Standard PLA Plus PLA Plus White
Izod and Charpy Impact Strength
Izod Impact Strength · 2026-10-11
Instrument readings in kJ/m²
Mean 4.646 kJ/m²; Std. Dev 0.23 kJ/m²; CV 4.96%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.
Charpy Impact Strength · 2026-10-11
Instrument readings in kJ/m²
Mean 3.522 kJ/m²; Std. Dev 0.307 kJ/m²; CV 8.711%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.
Thorwell Standard PLA White
Izod and Charpy Impact Strength
Charpy Impact Strength · 2026-10-10
Instrument readings in kJ/m²
Mean 3.06 kJ/m²; Std. Dev 0.049 kJ/m²; CV 1.608%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.
Izod Impact Strength · 2026-10-10
Instrument readings in kJ/m²
Mean 4.269 kJ/m²; Std. Dev 0.423 kJ/m²; CV 9.909%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.
Thorwell Standard PLA Yellow
Izod and Charpy Impact Strength
Charpy Impact Strength · 2026-10-10
Instrument readings in kJ/m²
Mean 3.024 kJ/m²; Std. Dev 0.179 kJ/m²; CV 5.925%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.
Izod Impact Strength · 2026-10-10
Instrument readings in kJ/m²
Mean 4.43 kJ/m²; Std. Dev 0.077 kJ/m²; CV 1.735%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.
Thorwell Standard Silk PLA Silk Blue
Izod and Charpy Impact Strength
Charpy Impact Strength · 2026-10-10
Instrument readings in kJ/m²
Mean 13.256 kJ/m²; Std. Dev 2.094 kJ/m²; CV 15.799%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.
Izod Impact Strength · 2026-10-10
Instrument readings in kJ/m²
Mean 9.968 kJ/m²; Std. Dev 1.503 kJ/m²; CV 15.076%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.
Thorwell Standard Wood PLA Wood Brown
Izod and Charpy Impact Strength
Izod Impact Strength · 2026-10-10
Instrument readings in kJ/m²
Mean 3.49 kJ/m²; Std. Dev 0.274 kJ/m²; CV 7.857%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.
Charpy Impact Strength · 2026-10-10
Instrument readings in kJ/m²
Mean 3.013 kJ/m²; Std. Dev 0.055 kJ/m²; CV 1.838%; Samples 10; Confidence 10
No break 0; invalid 0; excluded 0.
Comparative measurements; standard conformity unverified.
Thorwell Standard Blue TPE Blue
Flexible Material Testing
Comparative in-house measurements; n = independent specimens. Separate test groups; Overall unchanged.
| Method | Result | Condition | Mean | n | SD | CV % | Range | Not reached |
|---|---|---|---|---|---|---|---|---|
| eaacea91 | Apparent Compressive Stress at 20% Strain (MPa) | 10 s hold · 2 mm displacement · cycle 1 | 3.809 | 10 | 0.062 | 1.617 | 3.725–3.898 | 0 |
| eaacea91 | Apparent Compressive Stress at 20% Strain (MPa) | 30 s hold · 2 mm displacement · cycle 1 | 3.567 | 10 | 0.052 | 1.461 | 3.505–3.663 | 0 |
| eaacea91 | Compression Force at 20% Strain (N) | 10 s hold · 2 mm displacement · cycle 1 | 242.3 | 10 | 3.917 | 1.617 | 237–248 | 0 |
| eaacea91 | Compression Force at 20% Strain (N) | 30 s hold · 2 mm displacement · cycle 1 | 226.9 | 10 | 3.315 | 1.461 | 223–233 | 0 |
| eaacea91 | Force reduction from 10 s to 30 s at 20% Strain (%) | first compression only · 2 mm displacement | 6.346 | 10 | 1.272 | 20.038 | 4.979–9.677 | 0 |
| eaacea91 | Force retention at 20% Strain (%) | 10–30 s · 2 mm displacement · cycle 1 | 93.654 | 10 | 1.272 | 1.358 | 90.323–95.021 | 0 |
| eaacea91 | Residual height loss after recovery (%) | 20% compression · 30 s compressed hold · 60 s rest · 10 mm initial height · cycle 1 | 4 | 10 | 1.069 | 26.719 | 1–4.6 | 0 |
| ed381ba8 | Shore A Hardness (Shore A) | 10 s reading · 8 mm | 90.9 | 1 | — | — | 90.9–90.9 | 0 |
Shore location statistics
Within each specimen; specimen numbers are local to each test group. SD uses the sample formula. These readings do not increase independent n.
| Method | Scale | Condition | Specimen | Readings | Mean | Location SD | Location CV % |
|---|---|---|---|---|---|---|---|
| ed381ba8 | Shore A Hardness | 10 s reading · 8 mm | 1 | 5 | 90.9 | 1.025 | 1.127 |
Thorwell Standard Blue TPU Blue
Flexible Material Testing
Comparative in-house measurements; n = independent specimens. Separate test groups; Overall unchanged.
| Method | Result | Condition | Mean | n | SD | CV % | Range | Not reached |
|---|---|---|---|---|---|---|---|---|
| eaacea91 | Apparent Compressive Stress at 20% Strain (MPa) | 10 s hold · 2 mm displacement · cycle 1 | 3.942 | 10 | 0.08 | 2.031 | 3.835–4.103 | 0 |
| eaacea91 | Apparent Compressive Stress at 20% Strain (MPa) | 30 s hold · 2 mm displacement · cycle 1 | 3.724 | 10 | 0.078 | 2.101 | 3.631–3.898 | 0 |
| eaacea91 | Compression Force at 20% Strain (N) | 10 s hold · 2 mm displacement · cycle 1 | 250.8 | 10 | 5.095 | 2.031 | 244–261 | 0 |
| eaacea91 | Compression Force at 20% Strain (N) | 30 s hold · 2 mm displacement · cycle 1 | 236.9 | 10 | 4.977 | 2.101 | 231–248 | 0 |
| eaacea91 | Force reduction from 10 s to 30 s at 20% Strain (%) | first compression only · 2 mm displacement | 5.543 | 10 | 0.387 | 6.98 | 4.918–6 | 0 |
| eaacea91 | Force retention at 20% Strain (%) | 10–30 s · 2 mm displacement · cycle 1 | 94.457 | 10 | 0.387 | 0.41 | 94–95.082 | 0 |
| eaacea91 | Residual height loss after recovery (%) | 20% compression · 30 s compressed hold · 60 s rest · 10 mm initial height · cycle 1 | 1.21 | 10 | 0.185 | 15.313 | 0.9–1.5 | 0 |
| ed381ba8 | Shore A Hardness (Shore A) | 10 s reading · 8 mm | 90.1 | 1 | — | — | 90.1–90.1 | 0 |
Shore location statistics
Within each specimen; specimen numbers are local to each test group. SD uses the sample formula. These readings do not increase independent n.
| Method | Scale | Condition | Specimen | Readings | Mean | Location SD | Location CV % |
|---|---|---|---|---|---|---|---|
| ed381ba8 | Shore A Hardness | 10 s reading · 8 mm | 1 | 5 | 90.1 | 2.382 | 2.644 |
Score policy engineering-score-v70-1: Overall requires tensile, stiffness, consistency, layer adhesion and the Izod/Charpy impact family, each with equal weight. Both impact methods and configured versioned references are required. Missing results and unconfigured scores remain n/a. Legacy Impact is historical only; thermal remains separate. Engineering-axis counts describe displayed evidence, not Overall completeness.